Place of Origin: | CHINA |
---|---|
Brand Name: | KINTE |
Certification: | ROHS,ISO90001,ISO14000,Reach,Qualicoat |
Model Number: | NH6563 |
Minimum Order Quantity: | 500KG |
Price: | Negotiable |
Packaging Details: | 25kg/PE bag , 875KG/PALLET , 17,500KG/20GP |
Delivery Time: | 10 working days |
Payment Terms: | T/T, L/C, D/P |
Supply Ability: | 80,000 tons/year |
Specification: | HAA Cure | Application: | Powder Coating Required Durable |
---|---|---|---|
Advantage: | Low Curing Temperature,pinhole Free In Thicker Films | Rate: | 95/5 |
Curing Condition: | 160°C/15mins | Property: | Good Mechanical Property, Chemical Resistance And Anti-yellowing |
Highlight: | HAA Polyester,ISO90001 HAA Polyester,tgic free polyester powder coating |
Anti Yellowing Pinhole Free HAA Low Curing Temperature Polyester Resin NH6563
◇ Applications:
NH-6563 is a saturated carboxyl polyester resin designed for 95:5 Primid XL 552 powder coating to be cured at 160℃.
Advantages of powder coatings
1. Health and environmental protection
All kinds of liquid chemical harmful film-forming, dispersion, wetting, leveling, anti-corrosion and anti mildew additives added to achieve coating performance are omitted.
2. Convenient transportation and storage
Ordinary coatings contain about 20-50% water or solvent, while powder coatings are completely solid without water or solvent, which is convenient and safe for transportation. In addition, coatings containing water or solvent tend to freeze when the transportation and storage temperature is lower than 0 ℃. This problem does not exist in powder coatings.
3. No preservative is required
In the traditional liquid coating, there is both water and bacterial food, which is easy to be polluted by bacteria. Therefore, in order to prevent deterioration, preservatives should be added, while latex powder coatings have no bacterial pollution and do not need preservatives
4. Paint smell
Compared with the general traditional coating smell residue, this coating can disperse quickly, which can be said to disappear immediately.
◇ Basic features:
Low curing temp.
Outstanding mechanical properties
Good resistance to chemicals and fine anti-yellowing
Pinhole free in thicker films
◇ Specifications:
Appearance pale yellow flake
Color(50%DMF): max:2
Acid number(mgKOH/g): 30~34
Softening point(℃): 95~105
Glass transition temp.( ℃): ~58
Melting viscosity(200℃, cone/plate, mPa·s): 3800±700
Reactivity at 180℃(s, 5% XL552): 180±30
◇ Recommend Formulation:NH-6563
NH-6563 | Primid XL-552 | Filler & pigment | Leveling agent | Benzion |
200 | 12 | 140 | 2.4 | 1.2 |
◇ Extrusion Condition:
Two-screw extruder
Zone I: 90~110℃ Zone II: 110~120℃
Speed of revolution: 500~1200rpm
Fineness of powder: <100μm
◇ Application Condition:
Electrostatic spraying with: 40~70KV
Coating film thickness: 50~100μm
Degreased cold-rolled steel 0.5mm
◇ Curing Requirement: 160℃×15min.
◇ Film Properties:
Gel time(180℃,sec) 150~270
Flow(180℃,mm) 25~29
Gloss(60°): ≥85%
Bending(φ1mm): pass
Adhesive(1mm,grade): 0
Pencil hardness: 1H
Impact(50cm): pass
Storage test(40℃,24hr): good
Remarks:all the polyester resins could be customizes to Non-tin (A) ,anti gas burners(G),tribo gun(T) and anti-blooming(F)