| Place of Origin: | China |
|---|---|
| Brand Name: | KINTE |
| Certification: | ISO14000, ISO90001, Reach, Qualicoat, ROHS |
| Model Number: | NH6582-2 |
| Minimum Order Quantity: | 1000Kg |
| Price: | Negotiable |
| Packaging Details: | 25Kg/PE Bag, 875Kg/Pallet, 17,500Kg/20GP |
| Delivery Time: | 10 working days |
| Payment Terms: | L/C, D/P, T/T |
| Supply Ability: | 80,000 tons per year |
| Curing Type: | Polyester/Primid In Ratio 95:5 | Curing Time: | 180℃×10min |
|---|---|---|---|
| Acid Value (mgKOH/g): | 30~35 | Viscosity (mPa·s/200℃): | 4600~6000 |
| Softening Point (℃): | 100～110 | Glass Transition Temp. (℃): | ～61 |
| Properties: | Excellent Mechanical Properties | Application: | For 95:5 Primid XL 552 Powder Coating |
| Highlight: | Polyester HAA Resin,180 Degree Cure HAA Resin,Primid Powder Coating HAA Resin |
||
95/5 Polyester HAA Resin, 180 Degree Cure with Good Anti-yellowing for Primid Powder Coating
◎Introduction
NH-6582-2 is a saturated carboxyl polyester resin designed for 95:5 Primid XL 552 powder coating to be cured at 180℃.
Powder coatings are solid powder synthetic resin coatings composed of solid resins, pigments, fillers, and additives. Different from common solvent-based coatings and water-based coatings, its dispersion medium is not solvent and water, but air. It has the characteristics of no solvent pollution, 100% film formation, and low energy consumption. However, powder coatings are prone to pinhole formation compared to liquid coatings, which affects film performance and performance. In order to solve the problem of pinholes, benzoin is used to degas, but while benzoin eliminates pinholes, it is also easy to cause yellowing of the paint film.
While NH-6582-2 can solve the above two problems, there will be no pinholes during film formation, and also has good anti-yellowing performance.
◎Basic Features
Excellent mechanical properties
Good anti-yellowing
Pinhole free in thick films
Good weathering resistance and storage stability
◎Recommend Formulation: NH-6582/HAA
| NH-6582 | Primid XL-552 | Filler ＆ pigment | Leveling agent | Benzoin | 701 | 703 |
| 566 | 34 | 380 | 8 | 4 | 4 | 4 |
◎Specifications I
| Appearance | White or pale yellow transparent flakes |
| Color (50% DMF) | max:2 |
| Acid Number (mgKOH/g) | 30～35 |
| Softening Point (℃) | 100～110 |
| Glass Transition Temp. (℃) | ～61 |
| Melting Viscosity (200℃, cone/plate, mPa·s) | 5400±800 |
| Reactivity at 180℃ (s, 5% XL552) | 185±35 |
| Curing Requirement | 180℃×10min |
| Packaging | PE Bags, Net Weight 25kg ± 0.1kg / bag |
◎Specifications II
| Extrusion Condition | Two-screw Extruder | |
| Zone I: 90～110℃ | Zone II: 110～120℃ | |
| Speed of Revolution | 500～1200rpm | |
| Fineness of Powder | ＜100μm | |
| Application Condition | Electrostatic Spraying With | 40～70KV |
| Coating Film Thickness | 50～70μm | |
| Degreased Cold-rolled Steel | 0.5mm | |
| Film Properties | Gel Time (180℃, sec) | 120~200 |
| Horizontal Flow (180℃, mm) | 23~27 | |
| Gloss (60°) | ≥85% | |
| Bending (φ1mm) | Pass | |
| Adhesive (1mm, grade) | 0 | |
| Pencil Hardness | ≥1H | |
| Impact (50cm) | Pass | |
◎More Code
| Code | Ratio | Cure Cycle | Acid Value (mgKOH/g) | Viscosity (mPa.s/200℃) | Tg (℃) | Reactivity (s/180℃) | Properties |
| NH6582 | 95/5 | 180℃*10min | 30~35 | 4600~6000 | ~61 | 150~220 | Good storage stability, excellent mechanical properties and good outdoor durability. |
| NH6583 | 95/5 | 180℃*10min | 30~35 | 2500~3500 | ~56 | 200~290 | Very good flow, excellent mechanical properties, and pinhole free in thick films. |
| NH6584 | 95/5 | 180℃*10min | 30~36 | 2200~4200 | ~60 | 200~400 | Outstanding flow, excellent mechanical properties, cost effeciency. |
| NH6586-2 | 95/5 | 180℃*10min | 30~35 | 3000~4000 | ~59 | 280~480 | Good storage stability, excellent flow and mechanical properties. |
| NH6587 | 95/5 | 180℃*10min | 30~36 | 5000~7000 | ~67 | 120~280 | Excellent storage stability and mechanical properties, good outdoor durability and flow. |
◎Remarks: All the polyester resins could be customized to Non-tin (A), anti gas burners (G), tribo gun (T) and anti-blooming (F).